Experimental Study on Strength Characteristics of BlendedGeopolymer Mortar

Abstract

This study investigates the effect of fly ash (FA) class F content and curing temperature on the compressive strength of Geopolymer Mortar (GPLM). GPLM is produced from FA mixed with the alkaline solution. The experimental test was performed on GPLM cubeswith curing temperature of 70, 90 and 110 °C with curing period of one day. The alkaline activator was a combination of 12M NaOHsolution with sodium silicate in the ratio of 1:2.5. The ratio of alkaline solution to binder equal to 0.50. Test results indicate that theincrement in the FA content increases the compressive strength of GPLM. The strength increases with the increase of curingtemperature of GPLM. Moreover, blended GPLM with high percentage of fly ash has less sorptivity.

Bu çalışma, uçucu kül (FA) içeriğinin ve kür sıcaklığının Jeopolimer Harcın (GPLM) basınç dayanımı üzerindeki etkisiniaraştırmaktadır. GPLM, alkali çözelti ile karıştırılmış FA'dan üretilir. Deneysel test, bir günlük kürlenme süresi ile 70, 90 ve 110 ° Ckürleme sıcaklığı ile GPLM küpleri üzerinde gerçekleştirilmiştir. Alkalin aktivatör, 12M NaOH çözeltisinin 1: 2.5 oranında sodyumsilikat ile bir kombinasyonuydu. Alkali çözeltinin bağlayıcıya oranı 0,50'ye eşittir. Test sonuçları, FA içeriğindeki artışın GPLM'ninbasınç dayanımını artırdığını göstermektedir. GPLM'nin kürleme sıcaklığının artmasıyla mukavemet artar. Ayrıca, yüksek orandauçucu kül içeren harmanlanmış GPLM daha az sorptiviteye sahiptir.